- 1% Nickel alloyed wire ideal for high-strength and low-temperature applications.
- Offers exceptional impact toughness even at low temperatures.
- Provides good arc stability and penetration resulting in high-quality welds.
- Excellent mechanical properties at subfreezing temperatures down to -50°C.
- Widespread usage across diverse industries, including structural steel fabrication, pipeline construction, naval architecture, pressure vessel manufacturing, offshore installations, mechanical engineering, heavy-duty transportation and general metalworking
Additional Information
| Weight | 15 kg |
|---|---|
| Width | 0.8 cm |
| Material | Mild steel |
| Base materials | S355jr, s355j0, s355j2, s450j0, s355n s460n, s355nl s460nl, s355m s460m, s355ml s460ml, s460q, s460ql, p355gh, p355nh, p420nh, p460nh, p355n p460n, p355nh p460nh, l245nb l415nb, l245mb l485mb, l360qb l485qb, astm a 350 gr. lf1; a 516 gr. 65, 70; a 572 gr. 42, 50, 60, 65; a 573 gr. 65, 70; a 588 gr. b, c, k; a 633 gr. a, c, d, e; a 662 gr. b, c; a678 gr. b; a 707 gr. l2; a 841 gr. a, b, c; api 5 l x42, x52, x60, x65, x70, x52q, x60q, x65q, x70q |
| Temperature | ' 50ºc |
| Size | 0.8mm |
| Weight | 15kg |
| Shielding gas | Pure argon |
| Current type | Dc+ |
| Chemical composition (%) | Al = 0.02, c = 0.06 min 0.14 max, cr = 0.15, cu = 0.35, mo = 0.15, p = 0.020, s = 0.020, ti + zr = 0.15, v = 0.03, mn = 1.00 min 1.60 max, ni = 0.80 min 1.50 max, si = 0.50 min 0.90 max |
| Elongation | 26% |
| Tensile strength mpa | 600 |
| Yield strength mpa | 480 |
| Impact energy iso v | 100j |
| Grade | Er80s ni1 |
| Standards | Aws a5.28, en iso 14341 a: g 3ni1 |
| Set size | Single box |