- Low-alloyed solid wire designed for welding fine-grained, quenched and tempered high-strength steels.
- Provides a minimum yield strength of 690 MPa.
- Ideal choice for steels requiring high-strength and tough weld metal in critical applications.
- Excellent mechanical properties at subfreezing temperatures down to -40°C.
- Widely used in the construction of high-strength pipelines, earthmoving and mining equipment, trucks, mobile cranes, concrete pumps and lifting equipment.
!["Welding](http://parweld.co.uk/wp-content/uploads/2022/07/Welding-Positions-2-300x51.png")
Additional Information
| Width | 1.6 cm |
|---|---|
| Material | Low alloy |
| Base materials | T1, t1a, t1b, hy90, n a xtra 56 63 65 70, x65, x70, x80, s460, s500, s550, s620, s690, weldox |
| Temperature | ' 40ºc |
| Size | 1.6mm |
| Weight | 5kg |
| Shielding gas | Pure argon |
| Current type | Dc+ |
| Chemical composition (%) | C = 0.09, cr = 0.30, mn = 1.57, mo = 1.40, ni = 1.40, v = 0.09, si = 0.52 |
| Elongation | 19% (≥17%) |
| Tensile strength mpa | 800 (770 940) |
| Yield strength mpa | 750 (≥690) |
| 0.2% proof stress rp 0.2 | ?690mpa |
| Impact iso v | 70j (≥47j) |
| Grade | Er110s g |
| Standards | Aws a5.28: er110s g, en iso 16834 a: w 69 4 mn3ni1crmo |
| Set size | Single box |