Suitable for heat-resistant austenitic steels with high 25% Cr / 20% Ni contents. Provides a weld deposit that is fully austenitic and therefore requires minimal heat input during welding. Welding Positions: 
Additional Information
| Weight | 15 kg |
|---|---|
| Width | 0.8 cm |
| Material | Stainless steel |
| Temperature | 20?c |
| Size | 0.8mm |
| Weight | 15kg |
| Shielding gas | Pure argon |
| Current type | Dc+ |
| Elongation a5 | 45% |
| Tensile strength rm | 630 n/mm? |
| Yield strength rp 0.2 | 390 n/mm? |
| Yield strength rp 1.0 | 590 n/mm? |
| Impact energy iso v | 175j |
| Chemical composition(s) | B = 0.003 max, c = 0.080 min 0.120 max, co = 0.20 max, cr = 25.50 min 26.50 max, cu = 0.20 max, mn = 1.50 min 2.00 max, mo = 0.30 max, n = 0.60 max, nb = 0.50 max, ni = 20.50 min 21.00 max, p = 0.015 max, s = 0.015 max, si = 0.30 min 0.60 max |
| Grade | 310 |
| Set size | Single box |
| Standards | Aws a5.9 2012 er 310, en iso 14343 a:2009 g 25 20, en iso 14343 b:2009 ss 310 |