- Low-alloyed solid wire designed for welding fine-grained, quenched and tempered high-strength steels.
- Provides a minimum yield strength of 890 MPa.
- High impact strength at low temperatures with exceptional plasticity of the weld deposit.
- Excellent mechanical properties at subfreezing temperatures down to -40°C.
- Widely used in the construction of high-strength pipelines, earthmoving and mining equipment, trucks, mobile cranes, concrete pumps and lifting equipment.
Additional Information
| Weight | 15 kg |
|---|---|
| Length | 300 cm |
| Width | 0.8 cm |
| Material | Low alloy |
| Base materials | S890ql, s960q, p460nh, p460nl1, weldox 900, weldox 960, strenx 960 |
| Temperature | ' 40ºc |
| Size | 0.8mm |
| Spool | Bs300 |
| Weight | 15kg |
| Shielding gas | Mixed gas |
| Current type | Dc+ |
| Elongation | 16% (≥15%) |
| Tensile strength mpa | 1040 (940 1180) |
| 0.2% proof stress rp 0.2 | ?890mpa |
| Yield strength mpa | 960 (≥890) |
| Impact energy iso v | 60j (≥47j) |
| Chemical composition (%) | Al = 0.12, c = 0.13, cr = 0.20 min 0.60 max, cu = 0.30, mn = 1.60 min 2.10 max, mo = 0.30 min 0.65 max, ni = 2.30 min 2.80 max, p = 0.015, s = 0.018, si = 0.50 min 0.80 max, ti = 0.10, v = 0.03 min 0.13 max, zr = 0.10 |
| Grade | Fk1000 |
| Standards | A5.28: er120s g, en iso 16834 a: g 89 6 m21 mn4ni2crmo |
| Set size | Single box |